| C % | Ni% | Cr% | Mo% | Mn% | Si% | Fe % |
| ≦0.03 | 12 - 14 | 16 - 18 | 2.0 - 3.0 | ≦2.0 | ≦1.0 | Bal. |
| Parameter | Unit | Typical Value | Reference Range | Testing Method |
| Melt Index | g/10min | 100 | 80 - 200 | ISO 1133 (190 ℃, 21.6Kg) |
| Green Density | g/cm³ | 5.45 | 5.40 - 5.50 | ISO 3369 |
| Sintered Density | g/cm³ | 7.80 | 7.75 - 7.85 | ISO 3369 |
| Mold Factor | 1.165 | 1.163 - 1.168 | Mold Dimension / Product Dimension |
| Sintered State | Thermally Treated State | |
| Density | ≥7.80g/cm³ | |
| Yield Strength | ≥180MPa | ≥2000 MPa |
| Tensile Strength | ≥500MPa | ≥3000 MPa |
| Elongation | ≥50% | ≥12% |
| Hardness | 120 HV10 | ≥550 - 580 HV10 (35HRC) |
Multi-purpose Austenitic Stainless Steel. Suitable for machining larger MIM parts and replacing precision casting processes.