| C % | Ni % | Mo% | Cr% | P% | S% | V% | Fe % |
| 0.2 - 0.4 | 1.9 - 2.1 | 0.4 - 0.6 | 0.8 - 1.0 | ≦0.002 | ≦0.002 | Bal. |
| Parameter | Unit | Typical Value | Reference Range | Testing Method |
| Melt Index | g/10min | 200 | 150 - 300 | ISO 1133 (190 ℃, 21.6Kg) |
| Green Density | g/cm³ | 5.10 | 5.08 - 5.12 | ISO 3369 |
| Sintered Density | g/cm³ | 7.7 | 7.65 - 7.75 | ISO 3369 |
| Mold Factor | 1.190 | 1.185 - 1.195 | Mold Dimension / Product Dimension |
| Sintered State | Thermally Treated State | Thermally Treated State | |
| Density | ≥7.65g/cm³ | ||
| Yield Strength | ≥250MPa | ≥800 MPa | ≥1150 MPa |
| Tensile Strength | ≥350MPa | ≥900 MPa | ≥1300 MPa |
| Elongation | ≥5% | ≥3% | ≥2 % |
| Impact Value | ≥50J/m² | ||
| Hardness | 130 - 200 HV10 | ≥380 HV10（35 HRC） | ≥700 HV10（55 HRC） |
An advanced through - hardened versatile material. It's used in automotive parts, mechanical engineering, etc. Parts of this grade sintered in pure hydrogen can also be used as soft magnetic materials/parts of similar grades.