| C % | Ni % | Mo % | P % | S % | Fe % |
| 0.2-0.4 | 1.9-2.1 | 0.4-0.6 | ≤0.002 | ≤0.002 | Bal. |
| Parameter | Unit | Typical Value | Reference Range | Testing Method |
| Melt Index | g/10min | 700 | 600 - 1000 | ISO 1133 (190 ℃, 21.6Kg) |
| Green Density | g/cm³ | 5.10 | 5.08 - 5.12 | ISO 3369 |
| Sintered Density | g/cm³ | 7.7 | 7.65 - 7.75 | ISO 3369 |
| Mold Factor | 1.190 | 1.185 - 1.195 | Mold Dimension / Product Dimension |
| Sintered State | Thermally Treated State | ||
| Density | ≥7.65 g/cm3 | ||
| Yield Strength | ≥150 MPa | ≥550 MPa | ≥850 MPa |
| Tensile Strength | ≥250 MPa | ≥650 MPa | ≥1000 MPa |
| Elongation | ≥5% | ≥3% | ≥2 % |
| Impact Value | ≥8J/m² | ||
| Hardness | 120 - 180 HV10 | ≥350 HV10（25 HRC） | ≥600 HV10（55 HRC） |