| C % | Mo% | Cr% | P% | S% | Fe % |
| 0.4 - 0.6 | 0.4 - 0.6 | 1.0 - 1.2 | ≦0.002 | ≦0.002 | Bal. |
| Parameter | Unit | Typical Value | Reference Range | Testing Method |
| Melt Index | g/10min | 200 | 150 - 300 | ISO 1133 (190 ℃, 21.6Kg) |
| Green Density | g/cm³ | 5.10 | 5.08 - 5.12 | ISO 3369 |
| Sintered Density | g/cm³ | 7.80 | 7.70 - 7.90 | ISO 3369 |
| Mold Factor | 1.190 | 1.185 - 1.195 | Mold Dimension / Product Dimension |
| Sintered State | Thermally Treated State | Thermally Treated State | |
| Density | ≥7.70g/cm³ | ||
| Yield Strength | ≥300MPa | ≥900 MPa | ≥1200 MPa |
| Tensile Strength | ≥400MPa | ≥1000 MPa | ≥1400 MPa |
| Elongation | ≥5% | ≥3% | ≥2 % |
| Impact Value | ≥65J/m² | ||
| Hardness | 130 - 190 HV10 | ≥350 HV10 (35HRC) | ≥650 HV10 (55HRC) |
An advanced through - hardened versatile material. It's used in automotive parts, mechanical engineering, etc. Parts of this grade sintered in pure hydrogen can also be used as soft magnetic materials/parts of similar grades.